Double-sided semiconductor package and dual-mold method of making same

ABSTRACT

A semiconductor device comprises a first conductive layer formed on a carrier over an insulating layer. A portion of the insulating layer is removed prior to forming the first conductive layer. A first semiconductor die is disposed over the first conductive layer. A discrete electrical component is disposed over the first conductive layer adjacent to the first semiconductor die. A first encapsulant is deposited over the first conductive layer and first semiconductor layer. A conductive pillar is formed through the first encapsulant between the first conductive layer and second conductive layer. A second encapsulant is deposited around the first encapsulant, first conductive layer, and first semiconductor die. A second conductive layer is formed over the first semiconductor die, first encapsulant, and second encapsulant opposite the first conductive layer. The carrier is removed after forming the second conductive layer. A semiconductor package is mounted to the first conductive layer.

CLAIM OF DOMESTIC PRIORITY

The present application is a division of U.S. patent application Ser.No. 15/089,151, now U.S. Pat. No. 9,893,017, filed Apr. 1, 2016, whichclaims the benefit of U.S. Provisional Application No. 62/145,080, filedApr. 9, 2015, which applications are incorporated herein by reference.

FIELD OF THE INVENTION

The present invention relates in general to semiconductor devices and,more particularly, to a semiconductor device and method of forming adouble-sided semiconductor package using a dual-mold method.

BACKGROUND OF THE INVENTION

Semiconductor devices are commonly found in modern electronic products.Semiconductor devices vary in the number and density of electricalcomponents. Discrete semiconductor devices generally contain one type ofelectrical component, e.g., light emitting diode (LED), small signaltransistor, resistor, capacitor, inductor, and power metal oxidesemiconductor field effect transistor (MOSFET). Integrated semiconductordevices typically contain hundreds to millions of electrical components.Examples of integrated semiconductor devices include microcontrollers,microprocessors, and various signal processing circuits.

Semiconductor devices perform a wide range of functions such as signalprocessing, high-speed calculations, transmitting and receivingelectromagnetic signals, controlling electronic devices, transformingsunlight to electricity, and creating visual images for televisiondisplays. Semiconductor devices are found in the fields ofentertainment, communications, power conversion, networks, computers,and consumer products. Semiconductor devices are also found in militaryapplications, aviation, automotive, industrial controllers, and officeequipment.

Semiconductor devices exploit the electrical properties of semiconductormaterials. The structure of semiconductor material allows the material'selectrical conductivity to be manipulated by the application of anelectric field or base current or through the process of doping. Dopingintroduces impurities into the semiconductor material to manipulate andcontrol the conductivity of the semiconductor device.

A semiconductor device contains active and passive electricalstructures. Active structures, including bipolar and field effecttransistors, control the flow of electrical current. By varying levelsof doping and application of an electric field or base current, thetransistor either promotes or restricts the flow of electrical current.Passive structures, including resistors, capacitors, and inductors,create a relationship between voltage and current necessary to perform avariety of electrical functions. The passive and active structures areelectrically connected to form circuits, which enable the semiconductordevice to perform high-speed operations and other useful functions.

Semiconductor devices are generally manufactured using two complexmanufacturing processes, i.e., front-end manufacturing and back-endmanufacturing, each involving potentially hundreds of steps. Front-endmanufacturing involves the formation of a plurality of die on thesurface of a semiconductor wafer. Each semiconductor die is typicallyidentical and contains circuits formed by electrically connecting activeand passive components. Back-end manufacturing involves singulatingindividual semiconductor die from the finished wafer and packaging thedie to provide structural support, electrical interconnect, andenvironmental isolation. The term “semiconductor die” as used hereinrefers to both the singular and plural form of the words, andaccordingly, can refer to both a single semiconductor device andmultiple semiconductor devices.

One goal of semiconductor manufacturing is to produce smallersemiconductor devices. Smaller devices typically consume less power,have higher performance, and can be produced more efficiently. Inaddition, smaller semiconductor devices have a smaller footprint, whichis desirable for smaller end products. A smaller semiconductor die sizecan be achieved by improvements in the front-end process resulting insemiconductor die with smaller, higher density active and passivecomponents. Back-end processes may result in semiconductor devicepackages with a smaller footprint by improvements in electricalinterconnection and packaging materials.

Another goal of semiconductor manufacturing is to control and limitwarpage during semiconductor package assembly. Package warpage cancreate stresses between package layers and lead to cracking orinterlayer delamination. Inherent stresses within a semiconductorpackage impact long-term board level reliability. Warpage issues areexacerbated by the trend toward smaller and finer pitched conductivetraces. Controlling warpage during package manufacturing increases partyield and reduces failure rate.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a printed circuit board (PCB) with different types ofpackages mounted to its surface;

FIGS. 2a-2d illustrate a semiconductor wafer with a plurality ofsemiconductor die separated by a saw street;

FIGS. 3a-3i illustrate a method of forming a sub-package to use as thebase of a double-sided package;

FIG. 4 illustrates a completed sub-package with encapsulant etched awayto expose a semiconductor die;

FIG. 5 illustrates a completed sub-package including multiple back-sideRDL layers;

FIG. 6 illustrates a completed sub-package including recessed contactpads;

FIG. 7 illustrates a completed sub-package with RDL layers formingintegrated passive devices (IPDs);

FIGS. 8a-8i illustrate formation of double-sided packages based on thesub-packages;

FIGS. 9a-9c illustrate completed double-sided packages; and

FIG. 10 illustrates the double-sided package as the bottom package of apackage-on-package device.

DETAILED DESCRIPTION OF THE DRAWINGS

The present invention is described in one or more embodiments in thefollowing description with reference to the figures, in which likenumerals represent the same or similar elements. While the invention isdescribed in terms of the best mode for achieving objectives of theinvention, those skilled in the art will appreciate that the disclosureis intended to cover alternatives, modifications, and equivalents as maybe included within the spirit and scope of the invention as defined bythe appended claims and claims equivalents as supported by the followingdisclosure and drawings.

Semiconductor devices are generally manufactured using two complexmanufacturing processes: front-end manufacturing and back-endmanufacturing. Front-end manufacturing involves the formation of aplurality of die on the surface of a semiconductor wafer. Each die onthe wafer contains active and passive electrical components, which areelectrically connected to form functional electrical circuits. Activeelectrical components, such as transistors and diodes, have the abilityto control the flow of electrical current. Passive electricalcomponents, such as capacitors, inductors, and resistors, create arelationship between voltage and current necessary to perform electricalcircuit functions.

Passive and active components are formed over the surface of thesemiconductor wafer by a series of process steps including doping,deposition, photolithography, etching, and planarization. Dopingintroduces impurities into the semiconductor material by techniques suchas ion implantation or thermal diffusion. The doping process modifiesthe electrical conductivity of semiconductor material in active devicesby dynamically changing the semiconductor material conductivity inresponse to an electric field or base current. Transistors containregions of varying types and degrees of doping arranged as necessary toenable the transistor to promote or restrict the flow of electricalcurrent upon the application of the electric field or base current.

Active and passive components are formed by layers of materials withdifferent electrical properties. The layers can be formed by a varietyof deposition techniques determined in part by the type of materialbeing deposited. For example, thin film deposition can involve chemicalvapor deposition (CVD), physical vapor deposition (PVD), electrolyticplating, and electroless plating processes. Each layer is generallypatterned to form portions of active components, passive components, orelectrical connections between components.

Back-end manufacturing refers to cutting or singulating the finishedwafer into the individual semiconductor die and packaging thesemiconductor die for structural support, electrical interconnect, andenvironmental isolation. To singulate the semiconductor die, the waferis scored and broken along non-functional regions of the wafer calledsaw streets or scribes. The wafer is singulated using a laser cuttingtool or saw blade. After singulation, the individual semiconductor dieare mounted to a package substrate that includes pins or contact padsfor interconnection with other system components. Contact pads formedover the semiconductor die are then connected to contact pads within thepackage. The electrical connections can be made with conductive layers,bumps, stud bumps, conductive paste, or wirebonds. An encapsulant orother molding material is deposited over the package to provide physicalsupport and electrical isolation. The finished package is then insertedinto an electrical system and the functionality of the semiconductordevice is made available to the other system components.

FIG. 1 illustrates electronic device 50 having a chip carrier substrateor PCB 52 with a plurality of semiconductor packages mounted on asurface of PCB 52. Electronic device 50 can have one type ofsemiconductor package, or multiple types of semiconductor packages,depending on the application. The different types of semiconductorpackages are shown in FIG. 1 for purposes of illustration.

Electronic device 50 can be a stand-alone system that uses thesemiconductor packages to perform one or more electrical functions.Alternatively, electronic device 50 can be a subcomponent of a largersystem. For example, electronic device 50 can be part of a tablet,cellular phone, digital camera, or other electronic device.Alternatively, electronic device 50 can be a graphics card, networkinterface card, or other signal processing card that can be insertedinto a computer. The semiconductor package can include microprocessors,memories, application specific integrated circuits (ASIC),microelectromechanical systems (MEMS), logic circuits, analog circuits,radio frequency (RF) circuits, discrete devices, or other semiconductordie or electrical components. Miniaturization and weight reduction areessential for the products to be accepted by the market. The distancebetween semiconductor devices may be decreased to achieve higherdensity.

In FIG. 1, PCB 52 provides a general substrate for structural supportand electrical interconnect of the semiconductor packages mounted on thePCB. Conductive signal traces 54 are formed over a surface or withinlayers of PCB 52 using evaporation, electrolytic plating, electrolessplating, screen printing, or other suitable metal deposition process.Signal traces 54 provide for electrical communication between each ofthe semiconductor packages, mounted components, and other externalsystem components. Traces 54 also provide power and ground connectionsto each of the semiconductor packages.

In some embodiments, a semiconductor device has two packaging levels.First level packaging is a technique for mechanically and electricallyattaching the semiconductor die to an intermediate substrate. Secondlevel packaging involves mechanically and electrically attaching theintermediate substrate to the PCB. In other embodiments, a semiconductordevice may only have the first level packaging where the die ismechanically and electrically mounted directly to the PCB.

For the purpose of illustration, several types of first level packaging,including bond wire package 56 and flipchip 58, are shown on PCB 52.Additionally, several types of second level packaging, including ballgrid array (BGA) 60, bump chip carrier (BCC) 62, land grid array (LGA)66, multi-chip module (MCM) 68, quad flat non-leaded package (QFN) 70,quad flat package 72, embedded wafer level ball grid array (eWLB) 74,and wafer level chip scale package (WLCSP) 76 are shown mounted on PCB52. In one embodiment, eWLB 74 is a fan-out wafer level package (Fo-WLP)and WLCSP 76 is a fan-in wafer level package (Fi-WLP). Depending uponthe system requirements, any combination of semiconductor packages,configured with any combination of first and second level packagingstyles, as well as other electronic components, can be connected to PCB52. In some embodiments, electronic device 50 includes a single attachedsemiconductor package, while other embodiments call for multipleinterconnected packages. By combining one or more semiconductor packagesover a single substrate, manufacturers can incorporate pre-madecomponents into electronic devices and systems. Because thesemiconductor packages include sophisticated functionality, electronicdevices can be manufactured using less expensive components and astreamlined manufacturing process. The resulting devices are less likelyto fail and less expensive to manufacture resulting in a lower cost forconsumers.

FIG. 2a shows a semiconductor wafer 120 with a base substrate material122, such as silicon, germanium, aluminum phosphide, aluminum arsenide,gallium arsenide, gallium nitride, indium phosphide, silicon carbide, orother bulk semiconductor material for structural support. A plurality ofsemiconductor die or components 124 is formed on wafer 120 separated bya non-active, inter-die wafer area or saw street 126 as described above.Saw street 126 provides cutting areas to singulate semiconductor wafer120 into individual semiconductor die 124. In one embodiment,semiconductor wafer 120 has a width or diameter of 100-450 millimeters(mm).

FIG. 2b shows a cross-sectional view of a portion of semiconductor wafer120. Each semiconductor die 124 has a back or non-active surface 128 andan active surface 130 containing analog or digital circuits implementedas active devices, passive devices, conductive layers, and dielectriclayers formed within the die and electrically interconnected accordingto the electrical design and function of the die. For example, thecircuit may include one or more transistors, diodes, and other circuitelements formed within active surface 130 to implement analog circuitsor digital circuits, such as digital signal processor (DSP), ASIC, MEMS,memory, or other signal processing circuit. Semiconductor die 124 mayalso contain integrated passive devices (IPDs), such as inductors,capacitors, and resistors, for RF signal processing. Back surface 128 ofsemiconductor wafer 120 may undergo an optional backgrinding operationwith a mechanical grinding or etching process to remove a portion ofbase material 122 and reduce the thickness of semiconductor wafer 120and semiconductor die 124.

An electrically conductive layer 132 is formed over active surface 130using PVD, CVD, electrolytic plating, electroless plating process, orother suitable metal deposition process. Conductive layer 132 includesone or more layers of aluminum (Al), copper (Cu), tin (Sn), nickel (Ni),gold (Au), silver (Ag), or other suitable electrically conductivematerial. Conductive layer 132 operates as contact pads electricallyconnected to the circuits on active surface 130. Conductive layer 132can be formed as contact pads disposed side-by-side a first distancefrom the edge of semiconductor die 124, as shown in FIG. 2b .Alternatively, conductive layer 132 can be formed as contact pads thatare offset in multiple rows such that a first row of contact pads isdisposed a first distance from the edge of the die, and a second row ofcontact pads alternating with the first row is disposed a seconddistance from the edge of the die.

Semiconductor wafer 120 undergoes electrical testing and inspection aspart of a quality control process. Manual visual inspection andautomated optical systems are used to perform inspections onsemiconductor wafer 120. Software can be used in the automated opticalanalysis of semiconductor wafer 120. Visual inspection methods mayemploy equipment such as a scanning electron microscope, high-intensityor ultra-violet light, or metallurgical microscope. Semiconductor wafer120 is inspected for structural characteristics including warpage,thickness variation, surface particulates, irregularities, cracks,delamination, and discoloration.

The active and passive components within semiconductor die 124 undergotesting at the wafer level for electrical performance and circuitfunction. Each semiconductor die 124 is tested for functionality andelectrical parameters, as shown in FIG. 2c , using a test probe head 136including a plurality of probes or test leads 138, or other testingdevice. Probes 138 are used to make electrical contact with nodes orconductive layer 132 on each semiconductor die 124 and provideelectrical stimuli to contact pads 132. Semiconductor die 124 respondsto the electrical stimuli, which is measured by computer test system 140and compared to an expected response to test functionality of thesemiconductor die. The electrical tests may include circuitfunctionality, lead integrity, resistivity, continuity, reliability,junction depth, ESD, RF performance, drive current, threshold current,leakage current, and operational parameters specific to the componenttype. The inspection and electrical testing of semiconductor wafer 120enables semiconductor die 124 that pass to be designated as known gooddie (KGD) for use in a semiconductor package.

In FIG. 2d , semiconductor wafer 120 is singulated through saw street126 using a saw blade or laser cutting tool 142 into individualsemiconductor die 124. The individual semiconductor die 124 can beinspected and electrically tested for identification of KGD postsingulation.

FIGS. 3a-3i illustrate formation of a sub-package with semiconductor die124 as part of the process of forming a double-sided semiconductorpackage using a dual-mold process. FIG. 3a shows a cross-sectional viewof a portion of a carrier or temporary substrate 160 containingsacrificial base material such as silicon, polymer, beryllium oxide,glass, or other suitable low-cost, rigid material for structuralsupport. An optional interface layer or double-sided tape 162 is formedover carrier 160 as a temporary adhesive bonding film, etch-stop layer,or thermal release layer.

Carrier 160 can be a round or rectangular panel with capacity formultiple semiconductor die 124. Carrier 160 may have a larger surfacearea than the surface area of semiconductor wafer 120. A larger carrierreduces the manufacturing cost of the semiconductor package as moresemiconductor die can be processed on the larger carrier, therebyreducing the cost per unit. Semiconductor packaging and processingequipment are designed and configured for the size of the wafer orcarrier being processed.

To further reduce manufacturing costs, the size of carrier 160 isselected independent of the size of semiconductor die 124 or the size ofsemiconductor wafer 120. That is, carrier 160 has a fixed orstandardized size, which can accommodate various size semiconductor die124 singulated from one or more semiconductor wafers 120. In oneembodiment, carrier 160 is circular with a diameter of 330 mm. Inanother embodiment, carrier 160 is rectangular with a width of 560 mmand length of 600 mm. Semiconductor die 124 may have dimensions of 10 mmby 10 mm, which are packaged using the standardized carrier 160.Alternatively, semiconductor die 124 may have dimensions of 20 mm by 20mm, which are packaged using the same standardized carrier 160.Accordingly, standardized carrier 160 can handle any size semiconductordie 124, which allows subsequent semiconductor processing equipment tobe standardized to a common carrier, i.e., independent of die size orincoming wafer size.

Semiconductor packaging equipment can be designed and configured for astandard carrier using a common set of processing tools, equipment, andbill of materials to process any semiconductor die size from anyincoming wafer size. The common or standardized carrier 160 lowersmanufacturing costs and capital risk by reducing or eliminating the needfor specialized semiconductor processing lines based on die size orincoming wafer size. By selecting a predetermined carrier size to usefor any size semiconductor die from all semiconductor wafers, a flexiblemanufacturing line can be implemented.

An insulating or passivation layer 164 is formed over carrier 160 andbonding layer 162. Insulating layer 164 is formed using PVD, CVD,printing, lamination, spin coating, spray coating, sintering, or thermaloxidation. Insulating layer 164 contains one or more layers of silicondioxide (SiO2), silicon nitride (Si3N4), silicon oxynitride (SiON),tantalum pentoxide (Ta2O5), aluminum oxide (Al2O3), Hafnium Oxide(HfO2), benzocyclobutene (BCB), polyimide (PI), polybenzoxazoles (PBO),polymer dielectric resist with or without fillers or fibers, solderresist, or other material having similar insulating and structuralproperties. In one embodiment, insulating layer 164 includes glasscloth, filler, or fiber, e.g., E-glass cloth, T-glass cloth, Al2O3, orsilica filler, for enhanced bending strength. In some embodiments,insulating layer 164 is a relatively dark color and substantiallyopaque.

An electrically conductive layer 166 is formed over insulating layer 164using a metal deposition process such as printing, PVD, CVD, sputtering,electrolytic plating, or electroless plating. In other embodiments,conductive layer 166 is a sheet of conductive material laminated overcarrier 160, bonding layer 162, and insulating layer 164, e.g., a copperfoil or resin coated copper sheet. Conductive layer 166 includes one ormore layers of Al, Cu, Sn, Ni, Au, Ag, or other suitable electricallyconductive material.

In FIG. 3b , conductive layer 166 is patterned into a plurality ofcontact pads and conductive traces distributed across carrier 160.Conductive layer 166 is patterned using a photoresist or printed maskfollowed by wet etching, dry etching, deep reactive-ion etching, oranother metal etching process. Conductive layer 166 forms a back-sideredistribution layer (RDL) for a double-sided package.

In some embodiments, conductive layer 166 is formed as a patterned layerusing a semi-additive process. In one embodiment, copper foil is thinnedprior to forming a photoresist layer, and a selective, semi-additiveplating process is used to form patterned conductive layer 166. In otherembodiments, a seed layer is used that includes Ti/Cu, titanium tungsten(TiW)/Cu, or a coupling agent/Cu. Another metal with good wet etchingselectivity, such as Ni, Au, or Ag, is optionally added to the seedlayer. The seed layer is deposited by sputtering, electroless plating,or by depositing laminated Cu foil combined with electroless plating. Asemi-additive process is completed, the photoresist is removed, and theportions of the seed layer which remain exposed are removed by etchingto leave conductive layer 166 as an RDL pattern.

Saw street 170 is located between locations where singulatedsemiconductor die 124 will be disposed to form separate sub-packages. Inone embodiment, conductive layer 166 is completely removed within thearea of saw street 170.

An insulating or passivation layer 174 is formed over insulating layer164 and conductive layer 166 using PVD, CVD, printing, lamination, spincoating, spray coating, sintering or thermal oxidation. Insulating layer174 contains one or more layers of SiO2, Si3N4, SiON, Ta2O5, Al2O3,polymer dielectric resist with or without fillers or fibers, or othermaterial having similar insulating and structural properties. In oneembodiment, insulating layer 174 includes a glass cloth, filler, orfiber, such as E-glass cloth, T-glass cloth, Al2O3, or silica filler,for enhanced bending strength. A portion of insulating layer 174 isremoved by LDA to expose conductive layer 166. Alternatively, a portionof insulating layer 174 is removed by an etching process through apatterned photoresist layer to expose conductive layer 166.

Collectively, insulating layers 164 and 174 and conductive layer 166constitute a build-up interconnect structure 180 formed over carrier160. Build-up interconnect structure 180 may include as few as one RDLor conductive layer, such as conductive layer 166, and one insulatinglayer, such as insulating layer 174. Additional insulating layers andRDL layers can be formed over insulating layer 174 to provide additionalvertical and horizontal electrical connectivity across the packageaccording to the design and functionality of later mounted semiconductordie and devices. Additional insulating and metal layers may be formedwithin build-up interconnect structure 180 to provide grounding and EMIshielding layers within the semiconductor package. Additional metallayers of build-up interconnect structure 180 may form passivecomponents, e.g., inductors, metal-insulator-metal (MIM) capacitors, andresistors. In one embodiment, build-up interconnect structure 180includes fine-pitched conductive traces with less than a 200 μm pitch.

A patterning or photoresist layer 190 is formed over build-upinterconnect structure 180 in FIG. 3d . A portion of photoresist layer190 is removed by a photolithography and etching process, or LDA, toform openings 192. Openings 192 are formed over the removed portions ofinsulating layer 174 and extending to contact pads of conductive layer166. In some embodiments, a conductive seed layer of Cu, Ti/Cu, TiW/Cu,Ni, NiV, Au, Al, or other suitable seed material is formed using apatterning and metal deposition process such as PVD, CVD, sputtering,electrolytic plating, and electroless plating prior to deposition ofphotoresist layer 190.

In FIG. 3e , an electrically conductive material is deposited intoopenings 192 of photoresist layer 190 using Cu plating, electrolyticplating, electroless plating, or other suitable metal deposition processto form conductive pillars or vertical interconnect structures 194. Inone embodiment, conductive material for pillars 194 is deposited to aheight greater than a thickness of photoresist layer 190, and abackgrinding, etching, or other planarization process is performed sothat a top surface of pillars 194 and photoresist layer 190 are coplanaras illustrated in FIG. 3e . In another embodiment, conductive pillars194 are 3-D metal posts formed by copper plating or copper stud bumps.

In FIG. 3f , remaining portions of photoresist layer 190 are strippedaway leaving conductive pillars or vertical interconnect structures 194.After stripping photoresist layer 190, portions of any used seed layeroutside conductive pillars 194 are etched away and a leakage descum isperformed. Conductive pillars 194 can have a cylindrical shape with acircular or oval cross-section, or conductive pillars 194 can have acubic shape with a rectangular cross-section. Other pillar 194cross-section shapes are used in other embodiments.

In some embodiments, build-up interconnect structure 180 and conductivepillars 194 are inspected and tested to be known good at the wafer levelby open/short probe or auto-scope inspection at the present interimstage, i.e., prior to mounting a semiconductor die. Leakage can betested at a sampling location. Screening for defective interconnectionsprior to mounting semiconductor die over build-up interconnect structure180 minimizes the number of KGD wasted over defective interconnectstructures.

In FIG. 3g , semiconductor die 124, as singulated from semiconductorwafer 120 in FIG. 2d , are disposed over build-up interconnect structure180 between conductive pillars 194. Semiconductor die 124 are KGD havingbeen tested prior to mounting the semiconductor die to insulating layer174. In some embodiments, die-attach adhesive 198 is deposited over backsurface 128 of semiconductor die 124 prior to disposing thesemiconductor die onto build-up interconnect structure 180. In otherembodiments, die-attach adhesive 198 is deposited onto insulating layer174 prior to disposing semiconductor die 124 onto insulating layer 174.Adhesive 198 can include epoxy resin, thermoplastic resin, acrylatemonomer, a hardening accelerator, organic filler, silica filler, orpolymer filler. Die-attach adhesive 198 is an adhesive film or paste.Die-attach adhesive 198 facilitates and strengthens the attachment ofsemiconductor die 124 to build-up interconnect structure 180.

Semiconductor die 124 has conductive pillars 200 formed over contactpads 132 prior to singulation from semiconductor wafer 120 using aphotoresist layer similar to how conductive pillars 194 are formed.Conductive pillars 200 extend to approximately the same height overbuild-up interconnect structure 180 as conductive pillars 194. In someembodiments, bond wires 202 are provided to couple select contact pads132 to conductive layer 166. Bond wires 202 are wedge bonded or studbumped conductive wires. Bond wires are formed of copper or other metalalloy wire as a three-dimensional interconnection. In other embodiments,only conductive pillars 200 and 194 are used, and contact pads 132 arecoupled to conductive layer 166 through the conductive pillars andsubsequently formed front-side RDL.

In some embodiments, one or more discrete components 204 are disposed onbuild-up interconnect structure 180 and electrically connected toconductive layer 166 using solder, solder paste, bond wires, or otherappropriate interconnect structure. In one embodiment, bond wires 202are provided to couple contact pads 132 of semiconductor die 124 tocontact pads of discrete component 204. Discrete components 204 includecapacitors, inductors, resistors, diodes, transistors, and otherdiscrete components in various embodiments.

In FIG. 3h , an encapsulant or molding compound 208 is deposited overbuild-up interconnect structure 180, semiconductor die 124, pillars 194and 200, discrete components 204, and bond wires 202 as an insulatingmaterial using a paste printing, compressive molding, transfer molding,liquid encapsulant molding, vacuum lamination, spin coating, or othersuitable applicator. In one embodiment, encapsulant 208 is depositedusing tape assisted transfer molding. Encapsulant 208 is deposited overand around semiconductor die 124, discrete components 204, andconductive pillars 194 and 200 to form a reconstituted wafer 210.Encapsulant 208 can be polymer composite material, such as epoxy resinwith filler, epoxy acrylate with filler, or polymer with proper filler.Encapsulant 208 is non-conductive and environmentally protects thesemiconductor device from external elements and contaminants.Encapsulant 208 also protects semiconductor die 124 from degradation dueto exposure to light.

In one embodiment, encapsulant 208 is deposited to a height overbuild-up interconnect structure 180 that is greater than a height ofconductive pillars 194, conductive pillars 200, and bond wires 202. Abackgrinding, mechanical planarization, chemical-mechanicalplanarization, or other etching or planarization process is used toremove portions of encapsulant 208 and create a surface 212 comprised ofthe top surface of encapsulant 208 coplanar with top surfaces of pillars194 and 200. Bond wires 202 remain completely covered by encapsulant208. In some embodiments, conductive pillars 194 and 200 are formed asconductive vias through encapsulant 208 after the encapsulant isdeposited, rather than as standalone conductive pillars formed using aseparate photoresist layer.

FIG. 3i shows reconstituted wafer 210 singulated through encapsulant208, build-up interconnect structure 180, and carrier 160 using a sawblade or laser cutting tool 216 to create individual sub-packages 220.Sub-packages 220 include one or more semiconductor die 124 and,optionally, one or more discrete components 204 on build-up interconnectstructure 180 and carrier 160. Pillars 194 and 200, bond wires 202, orboth, are provided for 3-D interconnection. Build-up interconnectstructure 180 is provided as a back-side RDL for the final package.Forming build-up interconnect structure 180 and other 3-D interconnectstructures on carrier 160 allows formation of fine-pitched RDL and 3-Dinterconnection with low warpage.

FIG. 4 illustrates a sub-package 240. Sub-package 240 is similar tosub-package 220. Sub-package 240 is formed without bond wires 202 orconductive pillars 200, instead relying on conductive pillars 194 for3-D interconnection. Encapsulant 208 is planarized down to insulatinglayer 134 using a backgrinding or etching process so that subsequentlyformed RDL layers are able to directly connect to contact pads 132without pillars 200. In some embodiments, portions of insulating layer134 over contact pads 132 are removed by etching, LDA, or otherappropriate processes to expose the contact pads for subsequentinterconnection after completion of sub-package 240. A top surface ofinsulating layer 134 is co-planar with top surfaces of conductivepillars 194 and encapsulant 208. In other embodiments, encapsulant 208is planarized to active surface 130 of semiconductor die 124, whichcompletely removes insulating layer 134. Active surface 130 is co-planarwith encapsulant 208 and conductive pillars 194. An additionalconductive via or pillar 242 is formed as a top-side contact to discretecomponent 204 either before or after backgrinding of encapsulant 208. Inone embodiment, LDA is used to expose contact pads of discrete component204 having a tin or copper finish.

FIG. 5 illustrates sub-package 260. Sub-package 260 is similar tosub-package 240 but includes build-up interconnect structure 262 insteadof build-up interconnect structure 180. Build-up interconnect structure262 includes conductive layer 266, insulating layer 268, conductivelayer 270, and insulating layer 274 in addition to conductive layer 166and insulating layer 174. Conductive layer 266 is formed directly oncarrier 160 and interface layer 262. Carrier 160 is removed insubsequent processing steps to expose conductive layer 266 as contactpads.

Insulating layer 268 is formed over conductive layer 266. Portions ofinsulating layer 268 over conductive layer 266 are removed to exposeconductive layer 266. Conductive layer 270 is formed on insulating layer268 and extending into the openings through insulating layer 268 tocontact conductive layer 266. Insulating layer 274 is formed overconductive layer 270. Openings are formed in insulating layer 274 toexpose conductive layer 270. Conductive layer 166 is formed overinsulating layer 274 and extending to conductive layer 270 through theopenings of insulating layer 274. Insulating layer 174 is formed overconductive layer 166. Utilizing more conductive layers stacked inbuild-up interconnect structure 262 allows more complex 3-Dinterconnection. More or less than three conductive layers are used onother embodiments.

Each of the conductive layers 266, 270, and 166 of build-up interconnectstructure 262 are formed using sputtering, electrolytic plating,electroless plating, or other suitable deposition process. Conductivelayers 266, 270, and 166 can each be one or more layers of Al, Cu, Sn,Ni, Au, Ag, titanium (Ti), tungsten (W), or other suitable electricallyconductive material. Conductive layers 266, 270, and 166 include lateralRDL and vertical conductive vias to provide vertical and horizontalconduction paths through build-up interconnect structure 262. Portionsof conductive layers 266, 270, and 166 are electrically common orelectrically isolated according to the design and function ofsemiconductor die 124 and additional semiconductor die subsequentlycoupled to sub-package 260. Insulating layers 268, 274, and 174 includeone or more layers of SiO2, Si3N4, SiON, Ta2O5, Al2O3, or other materialhaving similar structural properties. Portions of insulating layers 268,274, and 174 are removed to expose underlying conductive layers usingetching or LDA.

FIG. 6 illustrates sub-package 280, which is similar to sub-package 240but with build-up interconnect structure 282. In build-up interconnectstructure 282, a portion of insulating layer 164 is removed prior toformation of conductive layer 166. Conductive layer 166 extends throughopenings in insulating layer 164 to form recessed contact pads incontact with interface layer 162 or carrier 160. After removal ofcarrier 160 in subsequent process steps, the recessed portions ofconductive layer 166 are exposed through insulating layer 164 as contactpads without requiring additional LDA or etching of insulating layer164.

FIG. 7 illustrates sub-package 300 with IPDs formed by layers ofbuild-up interconnect structure 302. Conductive layer 166 is formed oninsulating layer 164 and patterned as necessary to interconnect thesubsequently formed conductive layers. A dielectric or insulating layer304 is formed over portion 166 a of conductive layer 166. A conductivelayer 306 is formed over insulating layer 304. Together, portion 166 aof conductive layer 166, insulating layer 304, and conductive layer 306form a MIM capacitor. Conductive layers 166 and 306 form the plates of acapacitor and insulating layer 304 is a capacitor dielectric between theplates.

A resistive layer 308 is also formed on insulating layer 164. Resistivelayer 308 is similar to conductive layer 166, but formed with propertiesdesigned to control electrical resistance for current through resistivelayer 308. In some embodiments, electrical resistance is increased byreducing a cross-section or increasing a length of resistive layer 308.In other embodiments, electrical resistance is increased by modifyingthe constituent materials of resistive layer 308. Resistive layer 308forms a resistor as part of build-up interconnect structure 302.

Insulating layer 310 is formed over conductive layer 166, insulatinglayer 304, conductive layer 306, and resistive layer 308. Portions ofinsulating layer 310 are removed using etching or LDA to exposeunderlying conductive layers for electrical contact. A conductive layer316 is formed over insulating layer 310 as electrical contacts forunderlying IPD and RDL structures, as well as to form additional IPDsand RDL. Portions 316 a of conductive layer 316 operate as contacts forMIM capacitor plates 166 a and 306. Conductive layer 306 is coupled upto surface 212 of sub-package 300 by a conductive pillar 194. Plate 166a is coupled elsewhere by conductive traces of conductive layer 166, notillustrated. Portions 316 b of conductive layer 316 form electricalcontacts to resistive layer 308 similarly. Portions 316 c of conductivelayer 316 are coiled to exhibit inductive properties, forming aninductor as part of build-up interconnect structure 302. Select portions316 c of conductive layer 316 extend through insulating layer 310 forexternal electrical connection.

Insulating layer 320 is conformally applied over conductive layer 316and insulating layer 310 to complete build-up interconnect structure302. Conductive pillars 194 are formed, and semiconductor die 124 isdisposed over build-up interconnect structure 302, as discussed above tocomplete sub-package 300.

FIGS. 8a-8i illustrate a process of using any of the above describedsub-packages to create a double-sided semiconductor package. In FIG. 8a, a plurality of sub-packages 240 is disposed over carrier 330 andoptional interface layer 332. Carrier 330 and interface layer 332 aresimilar to carrier 160 and interface layer 162. While sub-packages 240from FIG. 4 are illustrated, any of the above-described sub-packages areused in other embodiments. In some embodiments, sub-packages are createdby mixing and matching features of the above-described sub-packages,e.g., using bond wires 202 with build-up interconnect structure 262, orusing the IPDs of build-up interconnect structure 302 with the recessedpads of build-up interconnect structure 282.

Sub-packages 240 are placed on carrier 330 face-down. Active surface 130of semiconductor die 124 is oriented toward carrier 330. Conductivepillars 194 extend to carrier 330 or interface layer 332. Conductivepillars 200 similarly extend to carrier 330 or interface layer 332 inembodiments that use conductive pillars 200 over contact pads 132. Spacebetween each sub-package 240 is reserved as saw-streets 334.

In FIG. 8b , encapsulant 336 is deposited over carrier 330 using a pasteprinting, compressive molding, transfer molding, liquid encapsulantmolding, vacuum lamination, spin coating, or other suitable applicator.Encapsulant 336 can be polymer composite material, such as epoxy resinwith filler, epoxy acrylate with filler, or polymer with proper filler.Encapsulant 336 and sub-packages 240 form a reconstituted wafer or panel340. Encapsulant 336 is present at the back-side of each sub-package 240over carrier 160 and also between each sub-package 240. Each sub-package240 is embedded in encapsulant 336. Build-up interconnect structure 180is embedded in encapsulant 336. Encapsulant 336 completely covers sidesurfaces of sub-packages 240 and build-up interconnect structures 180.Using a second encapsulant 336 in addition to encapsulant 208 increasesthe warpage tuning capability during subsequent formation of front-sideRDL.

In FIG. 8c , reconstituted wafer 340 is flipped and disposed on carrier350, including optional interface layer 352. Carrier 330 and interfacelayer 332 are removed by chemical etching, mechanical peeling, CMP,mechanical grinding, thermal bake, UV light, laser scanning, or wetstripping to expose encapsulant 208, encapsulant 336, conductive pillars194, conductive via 242, insulating layer 134, and contact pads 132.Conductive pillars 200 are exposed, rather than contact pads 132 andinsulating layer 134, in embodiments that use conductive pillars 200. Insome embodiments, portions of encapsulant 208, encapsulant 336, orinsulating layer 134 over contact pads 132 are removed by etching or LDAto expose contact pads 132.

In FIG. 8d , an insulating or passivation layer 372 is formed overencapsulant 336, encapsulant 208, conductive pillars 194, conductive via242, insulating layer 134, and contact pads 132 using PVD, CVD,printing, spin coating, spray coating, screen printing or lamination.Insulating layer 372 can be one or more layers of SiO2, Si3N4, SiON,Ta2O5, Al2O3, or other material having similar insulating and structuralproperties. In one embodiment, insulating layer 372 is a photosensitivedielectric polymer low-cured at less than 200° C. A portion ofinsulating layer 372 is removed by an etching process with a patternedphotoresist layer or by LDA to form openings over and exposing contactpads 132, conductive pillars 194, and conductive via 242. In someembodiments, a portion of insulating layer 372 in saw street 334 isremoved.

An electrically conductive layer or RDL 374 is formed over insulatinglayer 372, contact pads 132, conductive pillars 194, and conductive via242 using a patterning and metal deposition process such as printing,PVD, CVD, sputtering, electrolytic plating, and electroless plating.Conductive layer 374 can be one or more layers of Al, Cu, Sn, Ti, Ni,Au, Ag, W, or other suitable electrically conductive material. A portionof conductive layer 374 extends horizontally along insulating layer 372and parallel to active surface 130 of semiconductor die 124 to laterallyredistribute the electrical signals between contact pads 132, conductivepillars 194, and conductive via 242. Conductive layer 374 extendsvertically into openings of insulating layer 372 to contact pads 132,conductive pillars 194, and conductive via 242. In one embodiment,conductive layer 374 is etched or patterned to completely removeconductive layer 374 within saw street 334.

In FIG. 8e , an insulating or passivation layer 376 is formed overinsulating layer 372 and conductive layer 374 using PVD, CVD, printing,spin coating, spray coating, screen printing or lamination. Insulatinglayer 376 can be one or more layers of SiO2, Si3N4, SiON, Ta2O5, Al2O3,or other material having similar insulating and structural properties.In one embodiment, insulating layer 376 is a photosensitive dielectricpolymer low-cured at less than 200° C. A portion of insulating layer 376is removed by an etching process with a patterned photoresist layer orby LDA to form openings exposing conductive layer 374. In oneembodiment, insulating layer 376 is completely removed in saw street334.

An electrically conductive layer or RDL 378 is formed over insulatinglayer 376 and conductive layer 374 using a patterning and metaldeposition process such as printing, PVD, CVD, sputtering, electrolyticplating, and electroless plating. Conductive layer 378 can be one ormore layers of Al, Cu, Sn, Ti, Ni, Au, Ag, W, or other suitableelectrically conductive material. A portion of conductive layer 378extends horizontally along insulating layer 376 and parallel to activesurface 130 of semiconductor die 124 to laterally redistribute theelectrical interconnect to conductive layer 374. Conductive layer 378extends vertically through openings in insulating layer 376 to contactconductive layer 374. Portions of conductive layer 378 are electricallycommon or electrically isolated depending on the design and function ofthe semiconductor device. In some embodiments, conductive layer 378 iscompletely removed within saw street 334.

In FIG. 8f , an insulating or passivation layer 380 is formed overinsulating layer 376 and conductive layer 378 using PVD, CVD, printing,spin coating, spray coating, screen printing or lamination. Insulatinglayer 380 can be one or more layers of SiO2, Si3N4, SiON, Ta2O5, Al2O3,or other material having similar insulating and structural properties.In one embodiment, insulating layer 380 is a photosensitive dielectricpolymer low-cured at less than 200° C. A portion of insulating layer 380is removed by an etching process with a patterned photoresist layer orby LDA to form openings exposing conductive layer 378. In oneembodiment, insulating layer 380 is completely removed within saw street334.

An electrically conductive bump material is deposited over conductivelayer 378 in openings of insulating layer 380 using an evaporation,electrolytic plating, electroless plating, ball drop, or screen printingprocess. In one embodiment, the bump material is deposited with a balldrop stencil, without requiring a mask. The bump material can be Al, Sn,Ni, Au, Ag, Pb, Bi, Cu, solder, and combinations thereof, with anoptional flux solution. For example, the bump material can be eutecticSn/Pb, high-lead solder, or lead-free solder. The bump material isbonded to conductive layer 378 using a suitable attachment or bondingprocess. In one embodiment, the bump material is reflowed by heating thematerial above the material's melting point to form balls or bumps 382.In some applications, bumps 382 are reflowed a second time to improveelectrical contact to conductive layer 378. Bumps 382 can also becompression bonded or thermocompression bonded to conductive layer 378.In one embodiment, bumps 382 are formed over a UBM having a wettinglayer, barrier layer, and adhesion layer. Bumps 382 represent one typeof interconnect structure that can be formed over conductive layer 378.The interconnect structure can also use bond wires, conductive paste,stud bump, micro bump, or other electrical interconnect.

Collectively, insulating layers 372, 376, and 380, conductive layers 374and 378, and bumps 382 form a front-side build-up interconnect structure390 formed over reconstituted wafer 340. Build-up interconnect structure390 may include as few as one RDL or conductive layer, e.g., conductivelayer 374, and one insulating layer, such as insulating layer 372.Additional insulating layers and RDLs can be formed over insulatinglayer 380 prior to forming bumps 382, to provide additional vertical andhorizontal electrical connectivity across the reconstituted wafer 340according to the design and functionality of the semiconductor device.Additional insulating and metal layers may also be formed withinbuild-up interconnect structure 390 to provide grounding and EMIshielding layers within the semiconductor package. Build-up interconnectstructure 390 is inspected and tested to be known good at an interimstage, i.e., prior to additional device integration.

In FIG. 8g , a support carrier 400 and backgrinding tape 402 is appliedover build-up interconnect structure 390 and in contact with bumps 382.In some embodiments, backgrinding tape 402 is in contact with insulatinglayer 380. Carrier 350, a portion of encapsulant 336, and carrier 160are removed in a grinding operation using mechanical grinder 404. Insome embodiments, carrier 350 is removed by chemical etching, mechanicalpeeling, CMP, mechanical grinding, thermal bake, UV light, laserscanning, or wet stripping prior to removal of encapsulant 336 andcarrier 160 by grinder 404. The grinding operation exposes insulatinglayer 164 of sub-packages 240. After grinding, remaining portions ofencapsulant 336 around sub-packages 240 are coplanar with the surface ofinsulating layer 164 opposite semiconductor die 124.

In FIG. 8h , a portion of insulating layer 164 is removed to formopenings over and exposing conductive layer 166. Openings are formed byLDA using laser 416, etching, or other suitable process. Openingsthrough insulating layer 164 are configured to provide electricalinterconnect to semiconductor die or devices, for example, semiconductordie, memory devices, passive devices, saw filters, inductors, antenna,etc., stacked over semiconductor die 124. In one embodiment, a finishsuch as Cu organic solderability preservative (OSP) is applied to theexposed portions of conductive layer 166 to prevent Cu oxidation.

In FIG. 8i , reconstituted wafer 340 is singulated through build-upinterconnect structure 390 and encapsulant 336 using a saw blade orlaser cutting tool 422 into individual double-sided packages 430.

FIG. 9a illustrates a singulated double-sided package 430 removed fromcarrier 400. Semiconductor die 124 is electrically connected toconductive bumps 382 by RDL of front-side build-up interconnectstructure 390. Semiconductor die 124 is electrically connected tocontact pads of conductive layer 166 by front-side build-up interconnectstructure 390, conductive pillars 194, and back-side build-upinterconnect structure 180. Double-sided package 430 includes one ormore additional semiconductor packages mounted over back-side build-upinterconnect structure 180 and electrically connected to semiconductordie 124 through back-side build-up interconnect structure 180, pillars194, and front-side build-up interconnect structure 390. Double-sidedpackage 430 is disposed over a PCB or other substrate, e.g., PCB 52.Conductive bumps 382 are heated above a reflow temperature toelectrically and mechanically connect package 430 to contact pads on PCB52.

Double-sided package 430 is formed using a dual-mold approach. A firstmold is used to deposit encapsulant 208 around semiconductor die 124 andover back-side build-up interconnect structure 180. A second mold isused to embed back-side build-up interconnect structure 180 andencapsulant 208 in encapsulant 336. Encapsulant 336 is deposited afterformation of back-side build-up interconnect structure 180 and surroundsback-side build-up interconnect structure 180 during formation offront-side build-up interconnect structure 390 to give a manufacturer ofdouble-sided package 430 increased capability of adjusting for warpageduring formation of front-side build-up interconnect structure 390.

FIG. 9b illustrates double-sided package 436. double-sided package 436is similar to double-sided package 430 but insulating layer 164 iscompletely removed by grinder 404 in FIG. 8g . No separate LDA oretching step is used to expose conductive layer 166. Conductive layer166 is exposed for subsequent interconnection by the backgrinding stepin FIG. 8 g.

FIG. 9c illustrates double-sided package 440. Double-sided package 440is formed with back-side build-up interconnect structure 282, havingrecessed contact pads formed as part of conductive layer 166, ratherthan back-side build-up interconnect structure 180. Back-side build-upinterconnect structure 282 includes openings formed through insulatinglayer 164 prior to deposition and patterning of conductive layer 166.The grinding step in FIG. 8g exposes the portions of conductive layer166 that are recessed into the openings in insulating layer 164. Eventhough insulating layer 164 is not fully removed, contact pad portionsof conductive layer 166 are exposed by removal of encapsulant 336 andcarrier 160 with grinder 404.

FIG. 10 illustrates double-sided package 430 used as the bottom packageof a package-on-package device 460. A top package 462 is disposed overdouble-sided package 430. Top package 462 includes a semiconductor die474 disposed over an interposer or build-up interconnect structure 476.In some embodiments, interconnect structure 476 is a prefabricatedinterposer or PCB with semiconductor die 474 mounted to the interposer.In other embodiments, interconnect structure 476 is a build-upinterconnect structure formed over semiconductor die 474 similar tobuild-up interconnect structure 390. Interconnect structure 476 includesconductive layers 478 to fan-out electrical connections fromsemiconductor die 474 to locations aligning with contact pads ofconductive layer 166. Semiconductor die 474 includes contact pads 482coupled to conductive layers 478 of interconnect structure 476 byconductive bumps 484. An encapsulant 486 is disposed over semiconductordie 474 and interconnect structure 476 for environmental protection.Conductive bumps 490 formed over interconnect structure 476 are reflowedto electrically and mechanically couple top package 462 to double-sidedpackage 430 in a package-on-package formation.

Semiconductor die 474 is electrically coupled to semiconductor die 124through bumps 484, interconnect structure 476, bumps 490, back-sidebuild-up interconnect structure 180, conductive pillars 194, andfront-side build-up interconnect structure 390. Conductive bumps 382further connect both semiconductor die 474 and 124 to a PCB or substratethat package-on-package device 460 is mounted onto. Package-on-packagedevice 460 provides the functionality of both semiconductor die 124 andsemiconductor die 474 to a larger system or electronic device 50 formedon PCB 52.

While one or more embodiments of the present invention have beenillustrated in detail, the skilled artisan will appreciate thatmodifications and adaptations to those embodiments may be made withoutdeparting from the scope of the present invention as set forth in thefollowing claims.

What is claimed:
 1. A semiconductor device, comprising: a firstconductive layer; a semiconductor die disposed over the first conductivelayer; a conductive pillar formed over the first conductive layer; afirst encapsulant deposited over the first conductive layer andsemiconductor die; a second encapsulant deposited around the firstencapsulant, first conductive layer, and semiconductor die; and a secondconductive layer formed over the semiconductor die, first encapsulant,and second encapsulant opposite the first conductive layer, wherein theconductive pillar extends through the first encapsulant between thefirst conductive layer and second conductive layer.
 2. The semiconductordevice of claim 1, wherein the first conductive layer is formed over acarrier.
 3. The semiconductor device of claim 1, wherein the firstconductive layer is formed over an insulating layer.
 4. Thesemiconductor device of claim 3, wherein the insulating layer includesan opening and the first conductive layer extends into the opening. 5.The semiconductor device of claim 1, further including a discreteelectrical component disposed over the first conductive layer adjacentto the semiconductor die.
 6. The semiconductor device of claim 1,further including a semiconductor package mounted to the firstconductive layer.
 7. A semiconductor device, comprising: a substrateincluding an electrically conductive layer formed over the substrate; asemiconductor die disposed over the electrically conductive layer; afirst encapsulant deposited around the semiconductor die; a secondencapsulant deposited around the first encapsulant, substrate, andsemiconductor die; and a build-up interconnect structure formed over thesemiconductor die, the first encapsulant, and the second encapsulant,wherein the semiconductor die and first encapsulant are disposed betweenthe substrate and build-up interconnect structure, and the secondencapsulant extends over the substrate opposite the semiconductor die.8. The semiconductor device of claim 7, wherein the second encapsulantis deposited over the substrate opposite the semiconductor die.
 9. Thesemiconductor device of claim 7, further including an insulating layercomprising glass fibers or cloth formed on the substrate, wherein thesemiconductor die is disposed over the insulating layer.
 10. Thesemiconductor device of claim 7, wherein the second encapsulant isdeposited around the electrically conductive layer.
 11. Thesemiconductor device of claim 7, further including an interconnectstructure formed over the semiconductor die, first encapsulant, andsecond encapsulant opposite the electrically conductive layer.
 12. Thesemiconductor device of claim 7, further including a conductive pillarformed over the semiconductor die and within the first encapsulant. 13.The semiconductor device of claim 7, further including a bond wirecoupled between the semiconductor die and the electrically conductivelayer.
 14. A semiconductor device, comprising: an interconnectstructure; a first semiconductor die disposed over the interconnectstructure; a first encapsulant deposited over the first semiconductordie and including a side surface of the first encapsulant that iscoplanar with a side surface of the interconnect structure; a secondencapsulant deposited around the first semiconductor die, interconnectstructure, and first encapsulant; and a build-up interconnect structureformed over the first semiconductor die, first encapsulant, and secondencapsulant, wherein the first encapsulant and second encapsulant are indirect physical contact with the build-up interconnect structure. 15.The semiconductor device of claim 14, wherein the second encapsulantcovers the side surface of the first encapsulant and the side surface ofthe interconnect structure.
 16. The semiconductor device of claim 14,wherein the interconnect structure includes: an insulating layerincluding an opening formed through the insulating layer; and aconductive layer formed over the insulating layer and extending into theopening of the insulating layer.
 17. The semiconductor device of claim14, further including a conductive pillar formed over the interconnectstructure in the first encapsulant.
 18. The semiconductor device ofclaim 14, further including a second semiconductor die disposed over thefirst semiconductor die and electrically connected to the firstsemiconductor die through the interconnect structure.
 19. Thesemiconductor device of claim 14, further including a discreteelectrical component disposed over the interconnect structure adjacentto the semiconductor die.
 20. The semiconductor device of claim 14,further including a carrier, wherein the interconnect structure isformed on the carrier and the second encapsulant covers the carrier. 21.A semiconductor device, comprising: a first semiconductor die; a firstconductive layer formed over the first semiconductor die; a firstencapsulant deposited around the first semiconductor die and over firstconductive layer; a second encapsulant deposited around the firstencapsulant, first semiconductor die, and first conductive layer; asecond conductive layer formed over the first encapsulant and secondencapsulant opposite the first semiconductor die; and a conductivepillar disposed through the first encapsulant and coupled between thefirst conductive layer and the second conductive layer.
 22. Thesemiconductor device of claim 21, wherein the second encapsulantsurrounds the first encapsulant, first conductive layer, and firstsemiconductor die.
 23. The semiconductor device of claim 21, furtherincluding a second semiconductor die disposed over the firstsemiconductor die and coupled to the first semiconductor die through thefirst conductive layer.